(Which damage mechanism occurs primarily as a result of exposure of interior vessel surfaces to...

Comprehensive and Detailed Explanation From Exact Extract:

Polythionic acid stress corrosion cracking (PASCC) occurs when sulfide scales on stainless steel surfaces are exposed to oxygen and moisture, most commonly during shutdowns and outages.

Per API RP 571:

Polythionic acids form when iron sulfides react with air and water

Cracking occurs in austenitic stainless steels

Damage is most likely during shutdown, not normal operation

Therefore, PASCC is the damage mechanism directly associated with shutdown exposure conditions.

Referenced Documents (Study Basis):

API RP 571 – Section on Polythionic Acid Stress Corrosion Cracking

======================